Calcium Aluminate Siminti, Babban Aluminate Siminti A600, A700.G9, CA-70, CA-80

Takaitaccen Bayani

Ƙananan porosity, high sinadaran kwanciyar hankali, high zafin jiki yi, high lalacewa juriya

TUNTUBE YANZU

Siffofin

Ƙananan porosity, high sinadaran kwanciyar hankali, high zafin jiki yi, high lalacewa juriya

Cikakken bayani

Yawancin lokaci ana amfani da samfurin azaman kayan kiln daban-daban don ƙarfe, petrochemical, man fetur, injiniyoyi, kayan gini da sauran masana'antu.

Babban Simintin Alumina CA-50

Abubuwa			Naúrar	A600	A700	G9
Abubuwan sinadaran	Al₂O₃		%	50-60	50-60	53.5 max
	CaO		%	33 min	33.00 min	33.00 min
	SiO₂		%	8.00 max	8.00 max	5.50 max
	Fe₂O₃		%	2.50 max	2.50 max	2.50 max
	RO₂		%	0.4 max	0.40 max	0.40 max
Specific Surface Aea			cm³/g	3000 max	3000 max	350 min
Saitin Farko			min	60 min	60 min	90 min
Ƙarshen Saiti			h	6 max	6 max	6 min
Karfin Lankwasa		kwana 1	Mpa	5.50 max	7.00 min	8.00 min
Karfin Lankwasa		kwana 3	Mpa	6.50 max	8.00 min	10.00 min
Ƙarfin Ƙarfi		kwana 1	Mpa	40.00 max	50.00 min	72.00 min
Ƙarfin Ƙarfi		kwana 3	Mpa	50.00 max	60.00 min	82.00 min
Refractories			℃	1350	1350	1450

Calcium Alumina Cement

Abubuwa			Naúrar	CA-70	CA-80
Abubuwan sinadaran	Al₂O₃		%	68.50-72.00	78.50-81.00
	CaO		%	28.0-31.50	17.00-20.00
	SiO₂		%	≤0.50	≤0.40
	Fe₂O₃		%	≤0.50	≤0.30
	K₂O+Na₂O		%	≤0.50
Specific Surface Aea			Cm²/g	≥5000	≥7000
Saitin Farko			min	≥45	≥30
Ƙarshen Saiti			h	≤6	≤6
Karfin Lankwasa		24h ku	Mpa	≥7.0	≥5.50
M Ƙarfi		24h ku	Mpa	≥45	≥40
Refractories			℃	≥ 1600	≥1790